Free Delivery Over $100
|
|
|||
|
||||
OverviewThis thesis addresses elementary dislocation processes occurring in single-crystalline alloys based on Fe-Al, and investigates correspondences between dislocation distribution inside crystals characterized by transmission electron microscopy (TEM) and surface patterns observed using atomic force microscopy (AFM). Fe-Al alloys with different degrees of ordering were prepared and deformed in compression at ambient temperature in-situ inside the AFM device. The evolution of slip line structures was captured in the sequences of AFM images and wavy slip bands, while cross slip at the tip of the slip band and homogeneous fine slip lines were also identified. Further, the thesis develops a technique for constructing 3D representations of dislocations observed by TEM without the prohibitive difficulties of tomography, and creates 3D models of dislocation structures. Generally speaking, the thesis finds good agreement between AFM and TEM observations, confirming the value of AFM as a relevant tool for studying dislocations. Full Product DetailsAuthor: Jozef VeselýPublisher: Springer International Publishing AG Imprint: Springer International Publishing AG Edition: Softcover reprint of the original 1st ed. 2017 Dimensions: Width: 15.50cm , Height: 0.60cm , Length: 23.50cm Weight: 0.454kg ISBN: 9783319839103ISBN 10: 3319839101 Pages: 100 Publication Date: 07 July 2018 Audience: Professional and scholarly , Professional & Vocational Format: Paperback Publisher's Status: Active Availability: Manufactured on demand  We will order this item for you from a manufactured on demand supplier. Table of ContentsIntroduction.- Iron-Rich Iron Aluminides.- Experimental Methods.- Results.- Discussion.- Summary.ReviewsAuthor InformationTab Content 6Author Website:Countries AvailableAll regions |
||||