OverviewJute fiber reinforced PP-based composites (50% fiber by weight) were fabricated using compression molding and the physicomechanical properties were evaluated. Tensile strength, tensile modulus, elongation at break, flexural strength, flexural modulus, and impact strength of the composites were found to be 43.59 MPa, 6382.01 MPa, 81%, 21.85 MPa, 2550.97 MPa, and 45.49 N/m respectively. Then wood flour reinforced PP-based composites (50% fiber by weight) were fabricated and mechanical properties were equated with jute based composites. Jute-based composites showed excellent mechanical properties as compared to wood flour based composites. Also, the thermal properties like heat deflection temperature and flammability were found significantly good for jute based composites as compared with that of wood flour based composites. Full Product DetailsAuthor: Gokul Mahajan , Anil Maheshwari , D D ShindePublisher: LAP Lambert Academic Publishing Imprint: LAP Lambert Academic Publishing Dimensions: Width: 15.20cm , Height: 0.40cm , Length: 22.90cm Weight: 0.113kg ISBN: 9786202562812ISBN 10: 6202562811 Pages: 68 Publication Date: 27 June 2020 Audience: General/trade , General Format: Paperback Publisher's Status: Active Availability: In stock  We have confirmation that this item is in stock with the supplier. It will be ordered in for you and dispatched immediately. Table of ContentsReviewsAuthor InformationTab Content 6Author Website:Countries AvailableAll regions |
||||